Supercritical Foaming Material High Performance for Manufacturing Material Sample Sale
Supercritical Foaming Material High Performance for Manufacturing Material Sample Sale
Description
SHINCELL encourages healthy life style and provides attractive high performances products to meet high demanding and professional customer experience.
Respond® T series are innovative materials in sports and leisure fields, like premium yoga mats, shoes, sports ware and other sports equipment.
- All supercritical physical foaming, environmental protection without odor;
- No chemical residue；
- Closed cell structure,exquisite cells, nanoscale aperture diameter；
- Light weight, high strength, high elasticity, excellent mechanical properties;
- Non crosslinked, can be recyclable.
- Automotive,New energy battery,Transportation Packing,Consumer goods,Shoe material,Medical,Sports leisure
RESPOND® TPU:
RESPOND® TPU series are innovative TPU foam sheets,adopte new supercritical (CO2/N2) foaming technology,and not using chemical foaming agent in the production process.
- Pure physical foam made from TPU and Air
- No chemicals residual
- Extreme lighter,Great Resilience
- Odorless,Skin-friendly,and Comfortable Touching
- Excellent compression set
- Non-crosslinked,100%Recycle
- Apply to insole,midsole
RESPOND® TPEE:
MTPEE is microcellular TPEE foam, produced using TPEE as the
substrate with clean supercritical carbon dioxide as blowing agent
to form a large number of microcells in the matrix.
RESPOND® PEBAX:
MPEBA is microcellular PEBA foam, produced using PEBA as the substrate with clean supercritical carbon dioxide as blowing agent to form a large number of microcells in the matrix.
- Light weight
- Clean and environmental friendly
- Good cushion performance
- Excellent low temperature resistance
- Good chemical resistance
- Reusable
- Outstanding resilience
- PP:
- Our micro-cellular materials were produced by the foaming of polymers PP with advanced super-critical carbon dioxide technology.
M-PVDF:
PVDF has outstanding resistance to a wide range of aggressive chemicals. It also offers excellent toughness, wide temperature tolerance (-40 to 160℃), high dielectric strength and excellent resistance to nuclear radiation, UV and ageing.
Typical Applications: The properties of SINEXTM V Series such as fire and chemical resistance, antifungal, thermal insulation, etc. make it an excellent solution in construction, aviation & aerospace, military, Li battery, semiconductor, petrochemical and pharmaceutical industries.
Specification
RESPOND® TPU series:
|
Property |
Test Method |
Unit |
TPU |
|
|
|
|
T16 |
T20 |
T13 |
T3.6 |
|||
|
Density |
ISO 845:2006 |
g/cm3 |
0.16 |
0.2 |
0.13 |
0.036-0.09 |
|
Hardness |
SATRA TM 205-16 |
Shore C |
27±3 |
35±3 |
23±3 |
80±3 |
|
Compression Set |
ASTM D395 |
% |
46 |
42 |
|
|
|
Tensile Strength |
ISO 1798:2008 |
MPa |
3.7 |
4.5 |
|
|
|
Elongation at break |
ISO 1798:2008 |
% |
300 |
400 |
|
|
|
Method A Tear Trouser Test |
ISO 8067:2008 |
Kg/cm2 |
2.5 |
3.0 |
|
|
|
Ball Resilience |
ASTM D3574 |
% |
63 |
60 |
62 |
20 |
|
Size |
|
mm |
1950*1250*20 |
1850*1200*18 |
2000*1300*24 |
2000*1300*25 |
RESPOND® PEBA Series:
|
Property |
Test Method |
Unit |
PEBA |
|
Density |
ISO 845:2006 |
g/cm3 |
0.08 |
|
Hardness |
SATRA TM 205-16 |
C |
35±3 |
|
Compression Set |
ASTM D395 |
% |
33 |
|
Tensile Strength |
ISO 1798:2008 |
MPa |
1.9 |
|
Elongation at break |
ISO 1798:2008 |
% |
290 |
|
Method A Tear Trouser Test |
ISO 8067:2008 |
Kg/cm2 |
1.6 |
|
Ball Resilience |
ASTM D3574 |
% |
80 |
|
Size |
|
mm |
1500*1200*30 |
RESPOND® TPEE series：
|
Property |
Test Method |
Unit |
PEBA |
|
Density |
ISO 845:2006 |
g/cm3 |
0.15±0.03 |
|
Hardness |
SATRA TM 205-16 |
C |
35-43 |
|
Compression Set |
ASTM D395 |
% |
35 |
|
Tensile Strength |
ISO 1798:2008 |
MPa |
2.6 |
|
Elongation at break |
ISO 1798:2008 |
% |
290 |
|
Method A Tear Trouser Test |
ISO 8067:2008 |
Kg/cm2 |
2.9 |
|
Ball Resilience |
ASTM D3574 |
% |
72 |
|
Size |
|
mm |
1300*1100*20 |
- PP:
|
Property |
Test Method |
Unit |
PP |
|||
|
MPP10 |
MPP15 |
MPP20 |
MPP25 |
|||
|
Density |
ISO 845:2006 |
g/cm3 |
90 |
60 |
45 |
36 |
|
Hardness |
SATRA TM 205-16 |
C |
81 |
75 |
66 |
55 |
|
Compression Set |
ASTM D395 |
% |
0.56 |
0.36 |
0.3 |
0.23 |
|
Bending Strength |
GB-T 8812.2-2007 |
MPa |
0.9 |
0.68 |
0.44 |
0.36 |
|
Bending modulus |
GB-T 8812.2-2007 |
MPa |
49 |
33 |
24 |
18 |
|
Size |
|
mm |
2200*1450*29 |
2400*1580*33 |
2600*1750*38 |
2900*2000*41 |
M-PVDF:
|
Property |
Test Method |
Unit |
Typical Value |
|
|
V50 |
V70 |
|||
|
Density |
ISO 845:2006 |
g/cm3 |
0.05 |
0.07 |
|
Hardness |
SATRA TM 205-16 |
Shore C |
37-39 |
40-42 |
|
Tensile Strength |
ISO 1798:2008 |
MPa |
0.98 |
1.19 |
|
Elongation at break |
ISO 1798:2008 |
% |
54.56 |
66 |
|
Method A Tear Trouser Test |
ISO 8067:2008 |
N/cm |
0.62 |
0.94 |
|
Method B Tear Trouser Test |
ISO 8067:2008 |
N/cm |
38.72 |
43.98 |
|
Ball Resilience |
ASTM D3574 |
% |
55.5 |
49.5 |
Case Pictures
Care
To maintain the beauty and integrity of your purchase, we recommend treating it with care. Simple maintenance practices, such as gentle washing and proper storage, can effectively preserve the longevity of your favorites. We encourage you to refer to the care instructions included with each item, designed to help you keep your purchase in top condition.
Design
Our dedication to excellence extends beyond materials; it encompasses the artistry and craftsmanship illustrated in every piece we create.