SHINCELL encourages healthy life style and provides attractive high performances products to meet high demanding and professional customer experience.

Respond® T series are innovative materials in sports and leisure fields, like premium yoga mats, shoes, sports ware and other sports equipment.

All supercritical physical foaming, environmental protection without odor;
No chemical residue；
Closed cell structure,exquisite cells, nanoscale aperture diameter；
Light weight, high strength, high elasticity, excellent mechanical properties;
Non crosslinked, can be recyclable.
Automotive,New energy battery,Transportation Packing,Consumer goods,Shoe material,Medical,Sports leisure

RESPOND® TPU:

RESPOND® TPU series are innovative TPU foam sheets,adopte new supercritical (CO2/N2) foaming technology,and not using chemical foaming agent in the production process.

Pure physical foam made from TPU and Air
No chemicals residual
Extreme lighter,Great Resilience
Odorless,Skin-friendly,and Comfortable Touching
Excellent compression set
Non-crosslinked,100%Recycle
Apply to insole,midsole

RESPOND® TPEE:

MTPEE is microcellular TPEE foam, produced using TPEE as the

substrate with clean supercritical carbon dioxide as blowing agent

to form a large number of microcells in the matrix.

RESPOND® PEBAX:

MPEBA is microcellular PEBA foam, produced using PEBA as the substrate with clean supercritical carbon dioxide as blowing agent to form a large number of microcells in the matrix.

Light weight
Clean and environmental friendly
Good cushion performance
Excellent low temperature resistance
Good chemical resistance
Reusable
Outstanding resilience

PP:
Our micro-cellular materials were produced by the foaming of polymers PP with advanced super-critical carbon dioxide technology.

M-PVDF:

PVDF has outstanding resistance to a wide range of aggressive chemicals. It also offers excellent toughness, wide temperature tolerance (-40 to 160℃), high dielectric strength and excellent resistance to nuclear radiation, UV and ageing.

Typical Applications: The properties of SINEXTM V Series such as fire and chemical resistance, antifungal, thermal insulation, etc. make it an excellent solution in construction, aviation & aerospace, military, Li battery, semiconductor, petrochemical and pharmaceutical industries.

Specification

RESPOND® TPU series:

Property	Test Method	Unit	TPU
Property	Test Method	Unit	T16	T20	T13	T3.6
Density	ISO 845:2006	g/cm3	0.16	0.2	0.13	0.036-0.09
Hardness	SATRA TM 205-16	Shore C	27±3	35±3	23±3	80±3
Compression Set	ASTM D395	%	46	42
Tensile Strength	ISO 1798:2008	MPa	3.7	4.5
Elongation at break	ISO 1798:2008	%	300	400
Method A Tear Trouser Test	ISO 8067:2008	Kg/cm2	2.5	3.0
Ball Resilience	ASTM D3574	%	63	60	62	20
Size		mm	1950125020	1850120018	2000130024	2000130025

RESPOND® PEBA Series:

Property	Test Method	Unit	PEBA
Density	ISO 845:2006	g/cm3	0.08
Hardness	SATRA TM 205-16	C	35±3
Compression Set	ASTM D395	%	33
Tensile Strength	ISO 1798:2008	MPa	1.9
Elongation at break	ISO 1798:2008	%	290
Method A Tear Trouser Test	ISO 8067:2008	Kg/cm2	1.6
Ball Resilience	ASTM D3574	%	80
Size		mm	1500120030

RESPOND® TPEE series：

Property	Test Method	Unit	PEBA
Density	ISO 845:2006	g/cm3	0.15±0.03
Hardness	SATRA TM 205-16	C	35-43
Compression Set	ASTM D395	%	35
Tensile Strength	ISO 1798:2008	MPa	2.6
Elongation at break	ISO 1798:2008	%	290
Method A Tear Trouser Test	ISO 8067:2008	Kg/cm2	2.9
Ball Resilience	ASTM D3574	%	72
Size		mm	1300110020

PP:

Property	Test Method	Unit	PP
Property	Test Method	Unit	MPP10	MPP15	MPP20	MPP25
Density	ISO 845:2006	g/cm3	90	60	45	36
Hardness	SATRA TM 205-16	C	81	75	66	55
Compression Set	ASTM D395	%	0.56	0.36	0.3	0.23
Bending Strength	GB-T 8812.2-2007	MPa	0.9	0.68	0.44	0.36
Bending modulus	GB-T 8812.2-2007	MPa	49	33	24	18
Size		mm	2200145029	2400158033	2600175038	2900200041

M-PVDF:

Property	Test Method	Unit	Typical Value
Property	Test Method	Unit	V50	V70
Density	ISO 845:2006	g/cm3	0.05	0.07
Hardness	SATRA TM 205-16	Shore C	37-39	40-42
Tensile Strength	ISO 1798:2008	MPa	0.98	1.19
Elongation at break	ISO 1798:2008	%	54.56	66
Method A Tear Trouser Test	ISO 8067:2008	N/cm	0.62	0.94
Method B Tear Trouser Test	ISO 8067:2008	N/cm	38.72	43.98
Ball Resilience	ASTM D3574	%	55.5	49.5

Case Pictures

Supercritical Foaming Material High Performance for Manufacturing Material Sample Sale